35CrMnSiA
Facebook
Twitter
LinkedIn
Description
Scope of supply of Aviation Group:
Round rods, steel plates, non-standard forgings, rings, seamless pipes, non-standard customization, welcome to inquire!
1. Introduction to 35CrMnSiA materials
35CrMnSiA is a low alloy ultra-high strength steel. It has good comprehensive mechanical properties after heat treatment, high strength, sufficient toughness, good hardenability, welding (preheating before welding), and processing and forming properties, but has low corrosion resistance and oxidation resistance. It is generally used after low temperature backtempering, isothermal quenching or after tempering.
2. Chemical composition of 35CrMnSiA
| alloy | % | Chromium Cr | Carbon C | Manganese Mn | Silicon Si | Phosphorus P | Sulfur S | Ni | 铜 with |
| 35crmnsia | Minimum value | 1.10 | 0.32 | 0.80 | 1.10 | – | – | – | – |
| Maximum value | 1.40 | 0.39 | 1.10 | 1.40 | 0.025 | 0.025 | 0.030 | 0.025 |
3. Mechanical properties of 35CrMnSiA
Tensile strength σb (MPa): ≥1620(165)
Yield strength σs (MPa): ≥1275(130)
35crmnsia pictures
35crmnsia pictures
Elongation δ5 (%): ≥9
Section shrinkage rate ψ (%): ≥40
Impact power Akv (J): ≥31
Impact toughness value αkv (J/cm²): ≥39(4)
Hardness: ≤241HB
Sample size: Sample
IV. 35CrMnSiA application field
35CrMnSiA is used to manufacture medium-speed, heavy-duty, high-strength, and high-strength components and high-strength components.
Manufacture various important parts with high load and high speed, such as gears, shafts, clutches, sprockets, grinding wheel shafts, sleeves, bolts, nuts, etc.
Manufacture parts with wear-resistant and low working temperatures, variable load welding components, such as blades, valve plates and non-corrosive pipeline pipes of high-pressure blowers.