15-7PH
Описание
Объем поставок авиационной группы:
Нестандартные поковки, круглые прутки, стальные листы, кольца, бесшовные трубы
- 15-7PH material introduction
After heat treatment, the hardness is higher and the corrosion resistance is better. The precipitated hardened steel type with copper added is developed by replacing 2% of chromium in 0Cr17Ni7Al steel with 2%-3% molybdenum. The basic performance is similar to that of 0Cr17Ni7Al steel, but the overall performance is better than that of 0Cr17Ni7Al steel. In the austenite state, it can withstand various cold forming and welding processes, and then heat treatment can obtain the highest strength
- 15-7PH chemical composition
| сплав | C | Mn | И | P | S | Cr | На сайте | Эл | Мо |
| 15-7ph | – | – | – | – | – | 14..0 | 6.50 | 0.75 | 2.0 |
| 0.09 | 1.0 | 1.0 | 0.04 | 0.03 | 16.0 | 7.75 | 1.50 | 3.0 |
- 15-7PH physical properties
| плотность | 7,85 г/см3 |
| Температура плавления | 1415-1450℃ |
| государство | Прочность на разрыв МПа | Предел текучести МПа | Удлинение после разрыва | Скорость усадки секции % | HB | HRC |
| Твердый раствор | – | – | – | – | ≤269 | ≤26 |
| 565℃ старение | ≥1210 | ≥1100 | ≥7 | ≥25 | ≥375 | ≥42 |
| 510℃ старение | ≥1320 | ≥1210 | ≥6 | ≥20 | ≥388 | ≥44 |
- 15-7PH application fields
Сварка и пайка сотовых пластин, авиационных перегородок и пряжек используется для изготовления тонкостенных конструкционных деталей авиации, различных емкостей, трубопроводов, пружин, мембран клапанов, осей судов, пластин компрессоров, деталей реакторов, а также разнообразного химического оборудования и других конструкционных деталей.