Descrição
Âmbito de fornecimento do Grupo de Aviação:
Peças forjadas não normalizadas, varões redondos, chapas de aço, anéis, tubos sem costura
- 05Cr17Ni4Cu4Nb introdução de materiais
05Cr17Ni4Cu4Nb alloy is a precipitated, hardened, martensite stainless steel composed of copper, niobium/cinnabar.
05Cr17Ni4Cu4Nb is a martensite precipitation hardened stainless steel with high strength, high hardness, good welding performance and corrosion resistance. It has been widely promoted and used in valves, shafts, chemical fibers, aerospace and other industries, and has high-strength components with certain corrosion resistance requirements.
- 05Cr17Ni4Cu4Nb Chemical Components
| liga | % | C | Mn | E | P | S | Cr | Em | Cu | Fe | Nb |
| 05Cr17Ni4Cu4Nb | Valor mínimo | – | – | – | – | – | 15.5 | 3.0 | 3.0 | margem | 0.15 |
| Valor máximo | 0.07 | 1.00 | 1.00 | 0.040 | 0.030 | 17.5 | 5.0 | 5.0 | 0.45 |
- 05Cr17Ni4Cu4Nb Desempenho físico
| densidade | 7,78g/cm3 |
| Ponto de fusão | 1400-1440℃ |
Mechanical properties of 05Cr17Ni4Cu4Nb alloy at room temperature:
| liga | Resistência à tração Rm N/mm2 |
Resistência ao escoamento RP0.2N/mm2 |
Alongamento A5 % |
Dureza Brinell HB |
| 480℃ de envelhecimento | ≥1310 | ≥1180 | ≥10 | ≥40 |
| 550℃ de envelhecimento | ≥1060 | ≥1000 | ≥12 | ≥35 |
| 580℃ de envelhecimento | ≥1000 | ≥865 | ≥13 | ≥31 |
| Efeito do envelhecimento de 620℃ | ≥930 | ≥325 | ≥16 | ≥28 |
After heat treatment, the mechanical properties of the product are more perfect, reaching a compressive strength of up to 1100-1300 mpa (160-190 ksi).
This grade cannot be used at temperatures above 300°C (572°F) or very low. It has good corrosion resistance to both the atmosphere and diluted acids or salts, and its corrosion resistance is the same as that of 304 and 430.
- 05Cr17Ni4Cu4Nb corrosion resistance
- The corrosion resistance of 05CR17NI4CU4NB alloy is better than any other standard hardenable stainless steel plate. In most cases, its corrosion resistance is no less than 304.
- Se houver risco de fissuração por corrosão sob tensão, a temperatura de envelhecimento mais elevada deve ser superior a 550°C (1022°F), de preferência 590°C (1094°F).
- A temperatura de têmpera no meio de cloreto é de 550°C-1022°F.
- A temperatura de têmpera em meio H2S é de 590°C-1094°F.
- É suscetível à corrosão ou à corrosão por fissuras na água do mar estática.
- A sua resistência à corrosão é a mesma que a do tipo 304L na indústria petroquímica, alimentar e do papel.
- 05Cr17Ni4Cu4Nb application field
- Plataforma marítima, convés de helicópteros, outras plataformas
- Indústria alimentar
- Indústria da pasta de papel e do papel
- Aeroespacial (lâminas de turbina)
- Componentes mecânicos
- Balde para resíduos nucleares