0Cr15Ni7Mo2Al
설명
항공 그룹의 공급 범위:
비표준 단조품, 원형 막대, 강판, 링, 이음매 없는 파이프
- Introduction to 0Cr15Ni7Mo2Al 자료
The precipitated hardened steel type with copper added with 0Cr15Ni7Mo2Al is developed by replacing 2% of chromium in 0Cr17Ni7Al steel with 2%-3% molybdenum. After heat treatment, the hardness is higher and the corrosion resistance is better. Its basic performance is similar to that of 0Cr17Ni7Al steel, but its comprehensive performance is better than that of it. In the austenite state, it can withstand various cold forming and welding processes, and then heat treatment can obtain the highest strength
- 0Cr15Ni7Mo2Al 화학 성분
| 합금 | C | Mn | 그리고 | P | S | Cr | In | Al | Mo |
| 0Cr15Ni7Mo2Al | – | – | – | – | – | 14.0 | 6.50 | 0.75 | 2.0 |
| 0.09 | 1.0 | 1.0 | 0.040 | 0.030 | 16.0 | 7.75 | 1.50 | 3.0 |
- 0Cr15Ni7Mo2Al Physical Properties
| 밀도 | 7.85g/cm3 |
| 녹는점 | 1415-1450℃ |
| 상태 | 인장 강도 MPa | 항복강도 MPa | 파단 후 연신율 | 섹션 수축률 % | HB | HRC |
| 견고한 솔루션 | – | – | – | – | ≤269 | ≤26 |
| 565℃ 숙성 | ≥1210 | ≥1100 | ≥7 | ≥25 | ≥375 | ≥42 |
| 510℃ 숙성 | ≥1320 | ≥1210 | ≥6 | ≥20 | ≥388 | ≥44 |
- 0Cr15Ni7Mo2Al heat treatment
There are three heat treatment systems: TH1050 state, RH950 state, and CH900 state in A state.
Status A
After 1050℃ solid solution treatment, water-cool or air-cool. The metallographic structure is characterized by austenite.
TH1050 Status
After 1050℃ solid solution treatment, keep it at 760℃±15℃ for 90 minutes, air-cooled, cooled to 15℃ or room temperature within 1 hour, keep it for 30 minutes, and then heated to 565℃±10℃, keep it air-cooled, also known as 565℃ aging. The metallographic structure is characterized by precipitation hardened martensite.
RH950 status
After 1050℃ solid solution treatment, it is kept at 955℃±15℃ for 10 minutes, air-cooled to room temperature, cooled to -73℃±6℃ within 24 hours, maintained for 8 hours, and then heated to 510℃±6℃, and maintained for 60 minutes air-cooled, also known as 510℃ aging. The metallographic structure is characterized by precipitation hardened martensite.
CH900 status
After 1050℃ solid solution treatment, the cold rolling was 60% deformation, heated to 490℃ for 60 minutes, and air-cooled to room temperature. Metallographic structure is characterized by precipitation hardened martensite
- 0Cr15Ni7Mo2Al performance
Process performance includes cold and hot processing properties, heat treatment properties and welding properties.
0Cr15Ni7Mo2Al cold and hot processing performance
0Cr15Ni7Mo2Al stainless steel has an austenitic structure in solid solution and can withstand cold processing, but they all have a high tendency to harden cold work. Therefore, cold rolling, cold stamping, etc. are mostly processed using a process method with fewer passes, large pressure and multiple intermediate solid solution treatments. Its hot processing is not difficult, and the suitable hot processing temperature is 950-1150℃.
0Cr15Ni7Mo2Al heat treatment performance
The heat treatment of 0Cr15Ni7Mo2Al stainless steel is relatively complicated and has very strict requirements. Only by controlling the specified temperature, time and cooling speed can ideal performance be achieved.
0Cr15Ni7Mo2Al welding performance
The welding of 0Cr15Ni7Mo2Al stainless steel is the same as that of ordinary stainless steel. Arc welding, resistance welding and gas protection welding can be used, among which gas protection welding is the best. Welding is generally carried out in the solid solution state of the material. There is no need to preheat before welding, and it is best to perform the full heat treatment after welding. When the weld requires high strength, most of them are used to use 0Cr17Ni7A1 steel wire with low δ-ferritic content; when the weld strength requirements are not high and the corrosion resistance requirements are high, austenitic stainless steel wire can be used.
- 0Cr15Ni7Mo2Al application field
허니콤 플레이트, 항공기 파티션 및 버클의 용접 및 브레이징은 항공기의 얇은 벽 구조 부품, 각종 용기, 파이프 라인, 스프링, 밸브 멤브레인, 선박 차축, 압축기 플레이트, 원자로 부품은 물론 다양한 화학 장비 및 기타 구조 부품을 제조하는 데 사용됩니다.