1. Introduction to GH2132 Materials
GH2132 alloy is a Fe-25Ni-15Cr-based high-temperature alloy, and is strengthened with molybdenum, titanium, aluminum, vanadium and trace boron. Below 650°C, it has high yield strength, long-lasting, creep strength, and has good processing plasticity and satisfactory welding properties. Suitable for manufacturing high-temperature bearing components for aircraft engines that work under 650°C for a long time, such as turbine discs, compressor discs, rotor blades and fasteners.
2. GH2132 physical properties
| 合金 | % | で | Cr | フェ | B | モ | V | C | ムン | そして | S | P | 銅 | アル | の |
| Gh2132 | 最小値 | 24 | 13.5 | マージン | 0.003 | 1 | 0.1 | – | – | – | – | – | – | – | 1.9 |
| 最大値 | 27 | 16 | 0.01 | 1.5 | 0.5 | 0.08 | 0.35 | 0.35 | 0.002 | 0.015 | 0.3 | 0.35 | 2.35 |
3. GH2132 physical properties
| 密度 | 融点 | 熱伝導率 | 比熱容量 | 弾性率 | せん断弾性率 | 抵抗率 | 線膨張係数 |
| g / cm3 | ℃ | λ/(W/m·℃) | J/kg·℃ | GPa | GPa | μΩ·m | a/10-6℃-1 |
| 7.99 | 1364-1424 | 14.2(100℃) | 0.914 | 15.7(20~100℃) |
GH2132 mechanical properties: (Minimum value of mechanical properties detected at 20℃)
| 合金の状態 | 引張強さ Rm N/mm |
収量
RP0.2 N/mm |
伸び
A5 % |
ブリネル硬度 HB |
| 固溶体状態 | 930 | 590 | 15 | ≤341 |
Heat treatment requirements
| Material variety | Heat treatment system |
| Bars, round cakes | 980~1000℃, 1~2h, oil-cooled +700~720℃, 12~16h, air-cooled |
| Hot rolled plate, cold rolled plate | 980~1000℃, air-cooled +700~720℃, 16h, air-cooled |
| Cold pull rod | 980~1000℃, 1~2h, oil-cooled +700~720℃, 16h, air-cooled |
| Ring blank | 980~990℃, 1~2h, oil-cooled +700~720℃, 15h, air-cooled |
| Cold drawing for cold heading | 980~1000℃, 1~2h, water-cooled or oil-cooled +700~720℃, 16h, air-cooled |
4. GH2132 production implementation standards:
| 標準 | Chemical composition | スティック | 鍛造品 | プレート | Silk material | パイプ | 鍛造品 |
| National Standards | GB/T14992 | GB/T14994
GB/T14993 |
GB/T14997GB/T14998 | GB/T14995
GB/T14996 |
GB/T15062 | ||
| Aviation industry standards | HB5189 | ||||||
| National Military Standards | Gjb2611
GJB3165 |
GJB3317 | GJB2612
GJB3167 |
GJB3020
GJB3782 |
V. GH2132 application fields
Application Overview and Special Requirements In aviation, it is mainly used for engine compressor discs, turbine discs, load bearing rings, receivers, shafts, fasteners, and plate welded bearing parts that work below 650°C. in the country, this alloy has been widely used in aviation.