SUS631
Description
Étendue de la fourniture du groupe Aviation :
Pièces forgées non standard, barres rondes, plaques d'acier, anneaux, tubes sans soudure
- Introduction to SUS631 Matériaux
SUS631 is an austenite-martensite precipitation hardened stainless steel developed based on 18-8CrNi, also known as controlled phase change stainless steel.
SUS631 is also a diffuse hardened stainless steel, with high strength and high hardness, fatigue resistance, good corrosion resistance and die forging, and rarely deformed when exposed to high temperatures. This steel has good performance and is especially suitable for aerospace and aerospace. This special alloy is also suitable for other fields with high strength and corrosion resistance requirements. At high temperatures to 316°C, the spring performance is still good. SUS631 is used in aerospace, chemical, petrochemical, papermaking and metal processing industries.
- Ingrédients chimiques
| alliage | C | Mn | Et | P | S | Cr | En | Al |
| SUS631 | – | – | – | – | – | 16.0 | 6.50 | 0.75 |
| 0.09 | 1.0 | 1.0 | 0.040 | 0.030 | 18.0 | 7.75 | 1.50 |
- Propriétés physiques
| densité | 7.65g/cm3 |
| Point de fusion | 1415-1450℃ |
Mechanical properties of SUS631 alloy at room temperature
| Jubao alloy | Résistance à la traction Rm N/mm2 |
Limite d'élasticité RP0,2N/mm2 |
Élongation A5 % |
Dureté Brinell HB |
| Solid melting 1000~1100℃ Quick cooling | ≤1030 | ≤380 | ≥20 | ≤229 |
| 565℃ vieillissement | ≥1140 | ≥960 | ≥5 | ≥363 |
| 510℃ vieillissement | ≥1230 | ≥1030 | ≥4 | ≥388 |
- Material properties
SUS631 is a hardened stainless steel with high strength and hardness, fatigue resistance, good corrosion resistance and die forging. After solid solution treatment, it is an unstable austenite structure with good plastic toughness and processability. After adjustment, the austenite precipitation of carbide phenol composition changes. After martensite transformation treatment, most of the structures are transformed into low-carbon tempered martensite with good toughness. This state is the use state of steel and has good medium-temperature mechanical properties. Corrosion resistance is better than general martensitic stainless steel.
- Application areas
Used in aerospace, chemical, petrochemical, papermaking and metal processing industries.