05Cr17Ni4Cu4Nb
Description
Étendue de la fourniture du groupe Aviation :
Pièces forgées non standard, barres rondes, plaques d'acier, anneaux, tubes sans soudure
- 05Cr17Ni4Cu4Nb introduction du matériel
05Cr17Ni4Cu4Nb alloy is a precipitated, hardened, martensite stainless steel composed of copper, niobium/cinnabar.
05Cr17Ni4Cu4Nb is a martensite precipitation hardened stainless steel with high strength, high hardness, good welding performance and corrosion resistance. It has been widely promoted and used in valves, shafts, chemical fibers, aerospace and other industries, and has high-strength components with certain corrosion resistance requirements.
- 05Cr17Ni4Cu4Nb Chemical Components
| alliage | % | C | Mn | Et | P | S | Cr | En | Cu | Fe | Nb |
| 05Cr17Ni4Cu4Nb | Valeur minimale | – | – | – | – | – | 15.5 | 3.0 | 3.0 | marge | 0.15 |
| Valeur maximale | 0.07 | 1.00 | 1.00 | 0.040 | 0.030 | 17.5 | 5.0 | 5.0 | 0.45 |
- 05Cr17Ni4Cu4Nb Performance physique
| densité | 7,78g/cm3 |
| Point de fusion | 1400-1440℃ |
Mechanical properties of 05Cr17Ni4Cu4Nb alloy at room temperature:
| alliage | Résistance à la traction Rm N/mm2 |
Limite d'élasticité RP0,2N/mm2 |
Élongation A5 % |
Dureté Brinell HB |
| 480℃ vieillissement | ≥1310 | ≥1180 | ≥10 | ≥40 |
| 550℃ vieillissement | ≥1060 | ≥1000 | ≥12 | ≥35 |
| 580℃ vieillissement | ≥1000 | ≥865 | ≥13 | ≥31 |
| Effet de vieillissement de 620℃ | ≥930 | ≥325 | ≥16 | ≥28 |
After heat treatment, the mechanical properties of the product are more perfect, reaching a compressive strength of up to 1100-1300 mpa (160-190 ksi).
This grade cannot be used at temperatures above 300°C (572°F) or very low. It has good corrosion resistance to both the atmosphere and diluted acids or salts, and its corrosion resistance is the same as that of 304 and 430.
- 05Cr17Ni4Cu4Nb corrosion resistance
- The corrosion resistance of 05CR17NI4CU4NB alloy is better than any other standard hardenable stainless steel plate. In most cases, its corrosion resistance is no less than 304.
- S'il existe un risque de fissuration par corrosion sous contrainte, la température de vieillissement la plus élevée doit être supérieure à 550°C (1022°F), de préférence à 590°C (1094°F).
- La température de trempe dans le milieu chlorure est de 550°C-1022°F.
- La température de trempe en milieu H2S est de 590°C-1094°F.
- Il est sensible à la corrosion ou à la corrosion fissurante dans l'eau de mer statique.
- Sa résistance à la corrosion est la même que celle de la nuance 304L dans les industries pétrochimique, alimentaire et papetière.
- 05Cr17Ni4Cu4Nb application field
- Plate-forme maritime, pont d'hélicoptère, autres plates-formes
- Industrie alimentaire
- Industrie du papier et de la pâte à papier
- Aérospatiale (pales de turbine)
- Composants mécaniques
- Seau à déchets nucléaires