05Cr17Ni4Cu4Nb
Descripción
Alcance del suministro de Aviation Group:
Piezas forjadas no normalizadas, varillas redondas, chapas de acero, anillos, tubos sin soldadura
- 05Cr17Ni4Cu4Nb material introduction
05Cr17Ni4Cu4Nb alloy is a precipitated, hardened, martensite stainless steel composed of copper, niobium/cinnabar.
05Cr17Ni4Cu4Nb is a martensite precipitation hardened stainless steel with high strength, high hardness, good welding performance and corrosion resistance. It has been widely promoted and used in valves, shafts, chemical fibers, aerospace and other industries, and has high-strength components with certain corrosion resistance requirements.
- 05Cr17Ni4Cu4Nb Chemical Components
| aleación | % | C | Mn | Y | P | S | Cr | En | Cu | Fe | Nb |
| 05Cr17Ni4Cu4Nb | Valor mínimo | – | – | – | – | – | 15.5 | 3.0 | 3.0 | margen | 0.15 |
| Valor máximo | 0.07 | 1.00 | 1.00 | 0.040 | 0.030 | 17.5 | 5.0 | 5.0 | 0.45 |
- 05Cr17Ni4Cu4Nb Rendimiento físico
| densidad | 7,78 g/cm3 |
| Punto de fusión | 1400-1440℃ |
Mechanical properties of 05Cr17Ni4Cu4Nb alloy at room temperature:
| aleación | Resistencia a la tracción Rm N/mm2 |
Límite elástico RP0,2N/mm2 |
Alargamiento A5 % |
Dureza Brinell HB |
| 480℃ envejecimiento | ≥1310 | ≥1180 | ≥10 | ≥40 |
| 550℃ envejecimiento | ≥1060 | ≥1000 | ≥12 | ≥35 |
| 580℃ envejecimiento | ≥1000 | ≥865 | ≥13 | ≥31 |
| Efecto de envejecimiento de 620℃ | ≥930 | ≥325 | ≥16 | ≥28 |
After heat treatment, the mechanical properties of the product are more perfect, reaching a compressive strength of up to 1100-1300 mpa (160-190 ksi).
This grade cannot be used at temperatures above 300°C (572°F) or very low. It has good corrosion resistance to both the atmosphere and diluted acids or salts, and its corrosion resistance is the same as that of 304 and 430.
- 05Cr17Ni4Cu4Nb corrosion resistance
- The corrosion resistance of 05CR17NI4CU4NB alloy is better than any other standard hardenable stainless steel plate. In most cases, its corrosion resistance is no less than 304.
- Si existe riesgo de agrietamiento por corrosión bajo tensión, la temperatura de envejecimiento superior debe ser superior a 550°C (1022°F), preferiblemente 590°C (1094°F).
- La temperatura de revenido en el medio clorado es de 550°C-1022°F.
- La temperatura de revenido en medio H2S es de 590°C-1094°F.
- Es susceptible a la corrosión o a la corrosión por fisuras en agua de mar estática.
- Su resistencia a la corrosión es la misma que la del grado 304L en la industria petroquímica, alimentaria y papelera.
- 05Cr17Ni4Cu4Nb application field
- Plataforma marítima, cubierta para helicópteros, otras plataformas
- Industria alimentaria
- Industria papelera
- Aeroespacial (álabes de turbina)
- Componentes mecánicos
- Cubo de residuos nucleares