GH625/GH3625
Beschreibung
Lieferumfang für Aviation Group
Schmiedestücke, Rundstangen, Stahlplatten, Ringe, nahtlose Rohre, Stahlplatten/Stahlbänder, Drahtschweißmaterial, bitte fragen Sie uns an!
1. Introduction to GH625/GH3625 materials
GH3625 (GH625) alloy is a solid solution-strengthening nickel-based deformation high-temperature alloy with molybdenum niobium as the main reinforcement element. It has excellent corrosion resistance and oxidation resistance. It has good tensile and fatigue properties from low temperature to 980 degrees Celsius, and is resistant to stress corrosion under salt spray atmosphere.
Durchführungsbestimmungen
GJB 1953-1994 “Specifications on Hot Rolled Rods for High Temperature Alloys for Rotating Parts of Aero Engines”
GJB 2611-1996 “Specifications for Cold Pulling Rods for High Temperature Alloys for Aviation”
GJB 2612-1996 “Specifications for Cold Drawing of High Temperature Alloys for Welding”
GJB 3020-1997 “Specifications for High Temperature Alloy Ring Bills for Aviation”
GJB 3165-1998 “Specifications on Hot Rolling and Forged Rods for Aviation Loading Parts”
GJB 3782-1999 “Specifications for High Temperature Alloy Rods for Aviation”
HB 5198-1982 “Deformed high-temperature alloy rods for aviation blades”
2. Chemische Bestandteile
| Legierungsmedaille | % | C | Cr | Co | Unter | Mo | Nb | Fe | Al | von | Und | Mn | S | P | Cu |
| Gh625/
Gh3625 |
Minimaler Wert | – | 20.0 | – | Remain
quantity |
8.0 | 3.15 | – | – | – | – | – | – | – | – |
| Maximaler Wert | 0.10 | 23.0 | 1.0 | 10.0 | 4.15 | 5.0 | 0.4 | 0.4 | 0.5 | 0.5 | 0.015 | 0.015 | 0.07 |
3. Physikalische Eigenschaften
| Dichte
g / cm3 |
Schmelzpunkt
℃ |
Wärmeleitfähigkeit
λ/(W/m·℃) |
Spezifische Wärmekapazität
J/kg·℃ |
Elastizitätsmodul
GPa |
Shear modulus
GPa |
Widerstandsfähigkeit
μΩ·m |
Poisson’s | Koeffizient der linearen Ausdehnung
a/10-6℃-1 |
| 8.44 | 1290
1350 |
12.1(100℃) | 430 | 205 | 79 | 1.28 | 0.308 | 12.3(20~100℃) |
4. Mechanical properties
(Minimum value of mechanical properties detected at 20°C [1] )
| Heat treatment method | Zugfestigkeit
σb/MPa |
Ausbeute der Ausbeute
σp0.2/MPa |
Dehnung
S5 /% |
Brinell-Härte
HBS |
| Behandlung von Mischkristallen | 830 | 410 | 30 | ≤290 |
V. Alloy characteristics :
It has excellent corrosion resistance to various corrosive media in the oxidation and reduction environments
Excellent resistance to pit and crevice corrosion and does not cause stress corrosion cracking due to chloride
Excellent resistance to inorganic acid corrosion, such as nitric acid, phosphoric acid, sulfuric acid, hydrochloric acid, and mixed acid of sulfuric acid and hydrochloric acid, etc.
Excellent resistance to corrosion of various inorganic acid mixed solutions
When the temperature reaches 40℃, it can show good corrosion resistance in hydrochloric acid solutions of various concentrations.
Good processability and welding properties, no cracking sensitivity after welding
Manufacturing certification for pressure vessels with wall temperatures between -196 and 450°C
6. Application areas
Components of organic chemical process processes containing chlorides, especially in the use of acid chloride catalysts
Cookers and bleaching tanks for the pulp and paper industry
Absorption towers, reheaters, flue gas inlet baffles, fans (wet), stirrers, deflectors and flue ducts in flue gas desulfurization system
Equipment and components for the manufacture of acid gas environments
Reaction of acetic acid and acetic anhydride
German 
English 
French 
Portuguese 
Japanese 
Russian 
Italian 
Spanish 
Arabic 
Korean