05Cr17Ni4Cu4Nb
Beschreibung
Lieferumfang der Aviation Group:
Nicht standardisierte Schmiedestücke, Rundstangen, Stahlplatten, Ringe, nahtlose Rohre
- 05Cr17Ni4Cu4Nb material introduction
05Cr17Ni4Cu4Nb alloy is a precipitated, hardened, martensite stainless steel composed of copper, niobium/cinnabar.
05Cr17Ni4Cu4Nb is a martensite precipitation hardened stainless steel with high strength, high hardness, good welding performance and corrosion resistance. It has been widely promoted and used in valves, shafts, chemical fibers, aerospace and other industries, and has high-strength components with certain corrosion resistance requirements.
- 05Cr17Ni4Cu4Nb Chemical Components
| Legierung | % | C | Mn | Und | P | S | Cr | Unter | Cu | Fe | Nb |
| 05Cr17Ni4Cu4Nb | Minimaler Wert | – | – | – | – | – | 15.5 | 3.0 | 3.0 | Marge | 0.15 |
| Maximaler Wert | 0.07 | 1.00 | 1.00 | 0.040 | 0.030 | 17.5 | 5.0 | 5.0 | 0.45 |
- 05Cr17Ni4Cu4Nb Physische Leistung
| Dichte | 7,78 g/cm3 |
| Schmelzpunkt | 1400-1440℃ |
Mechanical properties of 05Cr17Ni4Cu4Nb alloy at room temperature:
| Legierung | Zugfestigkeit Rm N/mm2 |
Streckgrenze RP0.2N/mm2 |
Dehnung A5 % |
Brinell-Härte HB |
| 480℃ Alterung | ≥1310 | ≥1180 | ≥10 | ≥40 |
| 550℃ Alterung | ≥1060 | ≥1000 | ≥12 | ≥35 |
| 580℃ Alterung | ≥1000 | ≥865 | ≥13 | ≥31 |
| Alterungseffekt von 620℃ | ≥930 | ≥325 | ≥16 | ≥28 |
After heat treatment, the mechanical properties of the product are more perfect, reaching a compressive strength of up to 1100-1300 mpa (160-190 ksi).
This grade cannot be used at temperatures above 300°C (572°F) or very low. It has good corrosion resistance to both the atmosphere and diluted acids or salts, and its corrosion resistance is the same as that of 304 and 430.
- 05Cr17Ni4Cu4Nb corrosion resistance
- The corrosion resistance of 05CR17NI4CU4NB alloy is better than any other standard hardenable stainless steel plate. In most cases, its corrosion resistance is no less than 304.
- Besteht die Gefahr von Spannungsrisskorrosion, muss die höhere Alterungstemperatur über 550°C (1022°F), vorzugsweise 590°C (1094°F), liegen.
- Die Anlasstemperatur im Chloridmedium beträgt 550°C-1022°F.
- Die Anlasstemperatur im H2S-Medium beträgt 590°C-1094°F.
- Es ist anfällig für Korrosion oder Risskorrosion in statischem Seewasser.
- Seine Korrosionsbeständigkeit ist die gleiche wie die der Sorte 304L in der Petrochemie, Lebensmittel- und Papierindustrie.
- 05Cr17Ni4Cu4Nb application field
- Maritime Plattform, Hubschrauberdeck, andere Plattformen
- Lebensmittelindustrie
- Zellstoff- und Papierindustrie
- Luft- und Raumfahrt (Turbinenschaufeln)
- Mechanische Komponenten
- Eimer für nukleare Abfälle